WCB |
Carbon Steel |
ASTM A216 |
Non-corrosive applications including water, oil and gases at temperatures between -20°F (-30°C) and +800°F (+425°C) |
Grade WCB |
LCB |
Low Temp |
ASTM A352 |
Low temperature applications to -50°F(-46°C). Not for use above +650°F (+340°C). |
Carbon Steel |
Grade LCB |
LCC |
Low Temp |
ASTM A352 |
Low temperature applications to -50°F (-46°C). Not for use above +650°F(+340°C). |
Carbon Steel |
Grade LCB |
LC1 |
Low Temp |
ASTM A352 |
Low temperature applications to -75°F (-59°C). Not for use above+650°F(+340°C). |
Carbon Steel |
Grade LC1 |
LC2 |
Low Temp |
ASTM A352 |
Low temperature applications to -100°F (-73°C). Not for use above +650°F (+340°C). |
Carbon Steel |
Grade LC2 |
LC3 |
31/2% Nickel |
ASTM A352 |
Low temperature applications to -150°F (-101°C). Not for use above +650°F (+340°C). |
Steel |
Grade LC3 |
WC6 |
11/4%Chrome |
ASTM A217 |
Non-corrosive applications including water, oil and gases at temperatures between -20°F (-30°C) and +1100°F (+593°C). |
1/2% Moly Steel |
Grade WC6 |
WC9 |
21/4%Chrome |
ASTM A217 |
Non-corrosive applications including water, oil and gases at temperatures between -20°F (-30°C) and +1100°F (+593°C). |
|
Grade WC9 |
C5 |
5%Chrome |
ASTM A217 |
Mild corrosive or erosive applications as well as non-corrosive applications at temperatures between -20°F (-30°C) and +1200°F (+649°C). |
1/2% Moly |
Grade C5 |
C12 |
9%Chrome |
ASTM A217 |
Mild corrosive or erosive applications as well as non-corrosive applications at temperatures between -20°F (-30°C) and +1200°F (+649°C). |
1% Moly |
Grade C12 |
CA6NM |
12% Chrome |
ASTM A487 |
Corrosive application at temperatures between -20°F (-30°C) and +900°F (+482°C). |
Steel |
Grade CA6NM |
CA15 |
12% Chrome |
ASTM A217 |
Corrosive application at temperatures up to +1300°F (+704°C) |
|
Grade CA15 |
CF8M |
316SS |
ASTM A351 |
Corrosive or either extremely low or high temperature non-corrosive services between -450°F (-268°C) and +1200°F (+649°C). Above +800°F (+425°C) specify carbon content of 0.04% or greater. |
Grade CF8M |
CF8C |
347SS |
ASTM 351 |
Primarily for high temperature, corrosive applications between -450°F (-268°C) and +1200°F (+649°C). Above +1000°F (+540°C) specify carbon content of 0.04% or greater. |
|
Grade CF8C |
CF8 |
304SS |
ASTM A351 |
Corrosive or extremely high temperatures non-corrosive services between -450°F (-268°C) and +1200°F (+649°C). Above +800°F (+425°C) specify carbon content of 0.04% or greater. |
Grade CF8 |
CF3 |
304L SS |
ASTM A351 |
Corrosive or non-corrosive services to +800F (+425°C). |
|
Grade CF3 |
CF3M |
316L SS |
ASTM A351 |
Corrosive or non-corrosive services to +800F (+425°C). |
Grade CF3M |
CN7M |
Alloy-20 |
ASTM A351 |
Good resistance to hot sulfuric acid to +800F (+425°C). |
|
Grade CN7M |
M-35 |
Monel |
ASTM 743 |
Weldable grade. Good resistance to corrosion by all common organic acids and salt water. Also highly resistant to most alkaline solutions to +750°F (+400°C). |
Grade M3-35-1 |
N-12M |
Hastelloy B |
ASTM A743 |
Is well suited for handling hydrofluoric acid at all concentrations and temperatures. Good resistance to sulphuric and phosphoric acids to +1200°F (+649°C). |
|
Grade N-12M |
CW12M |
Hastelloy C |
ASTM A743 |
Good resistance to strong oxidation conditions. Good properties at high temperatures. Good resistance to sulphuric and phosphoric acids to +1200°F (+649°C). |
Grade CW-12M |
CY-40 |
inconel |
ASTM A743 |
Very good for high temperature service. Good resistance to strongly corrosive media and atmosphere to +800°F (+425°C). |
|
Grade CY-40 |
B62 |
Bronze |
ASTM B62 |
Water, oil or gas: up to 400°F. Excellent for brine and seawater service. |